AISI F10012 Enquiry | Print this page
AISI F10012 Details
F10012
AISI F10012 Standard Download
| Category | Type | Grade | Microstructure | Designations |
|---|---|---|---|---|
| Grades | Cast Iron and Cast Steel | F10012 | Pearlitic | USA - AISI , ASTM A159-1993 | |
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | 3.10 | 3.60 | ||
| Si | 1.95 | 2.40 | ||
| Mn | 0.60 | 0.90 | ||
| P | - | 0.10 | ||
| S | - | 0.15 |
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 894 (≥) | 759 (≥) | 24 | 32 | 43 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 223 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 716 (≥) | 764 (≥) | 23 | 14 | 13 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 232 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 841 | 247 | 517 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
| Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |
| Grade | Standard | Country | Application |
|---|---|---|---|
| F10012 | AISI | USA | Used in the products of the automobile, truck, tractor, and allied industries. Diesel engine castings, liners, cylinders, and pistons. |