UNS Incoloy 800 Enquiry | Print this page
UNS Incoloy 800 Details
Cr content is usually 15-25% of the 800 alloy, nickel content is 30-45%, and contains a small amount of aluminum and titanium.800 alloy from high temperature fast cooling after all in a single austenite zone, therefore, using a state as a single austenitic organization.Alloy has the high chromium content and plenty of nickel content, so a higher resistance to high temperature corrosion performance, more in industrial application.In the chloride, low concentration of NaOH aqueous solution and high temperature and high pressure water, has good resistance to stress corrosion cracking performance, so the equipment used in the manufacture of resistance to stress corrosion cracking Incoloy800 similar brands China: 0 cr20ni32alti America: No8800 Japan: NCF800 west: X2NiCrAlTi3220 Incoloy800 nuclear generator application fields of chemical industry Nitric acid cooler, acetic anhydride, cracking tube heat exchange equipment heat exchange
UNS Incoloy 800 Standard Download
| Category | Type | Grade | Designations |
|---|---|---|---|
| Grades | Superalloys | Incoloy 800 | USA - UNS , ASTM B409 | ASTM B514 | ASTM B515 | |
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | - | 0.10 | ||
| Si | - | 1.00 | ||
| Mn | - | 1.50 | ||
| P | - | 0.030 | ||
| S | - | 0.015 | ||
| Cr | 19.00 | 23.00 | ||
| Ni | 30.00 | 35.00 | ||
| Fe | - | Bal |
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 794 (≥) | 644 (≥) | 21 | 41 | 24 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 444 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 919 (≥) | 211 (≥) | 42 | 42 | 12 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 421 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 969 | 651 | 978 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
| Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |
| Grade | Standard | Country | Application |
|---|---|---|---|
| Incoloy 800 | UNS | USA | Equipment used in the manufacture of resistance to stress corrosion cracking |
Relevant products
Incoloy 800 Equivalent Grade Stock
| Steel grade | Dimension | Shape | Unit | Quantity | Delivery state | Query |
|---|---|---|---|---|---|---|
| Incoloy800 round bar | Φ115*1400 | Round Bar | Kgs | 169 | Hot-Rolled+Annealed+black | Enquiry |