DIN 1.3802 Enquiry | Print this page
DIN 1.3802 Details
Steel castings - Austenitic manganese steel castings, 1-3802 GX120Mn13
DIN 1.3802 Standard Download
| Category | Type | Grade | Designations |
|---|---|---|---|
| Grades | Stainless Steels | 1.3802 | Germany - DIN , DIN EN 10349 | SEW 395 | |
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | 1.10 | 1.30 | ||
| Si | - | 0.50 | ||
| Mn | 11.50 | 13.50 | ||
| P | - | 0.060 | ||
| S | - | 0.030 | ||
| Cr | - | 0.50 |
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 824 (≥) | 949 (≥) | 43 | 42 | 32 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 341 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 669 (≥) | 921 (≥) | 21 | 21 | 44 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 321 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 333 | 693 | 487 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
| Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |
| Grade | Standard | Country | Application |
|---|---|---|---|
| 1.3802 | DIN | Germany | Steel castings - Austenitic manganese steel castings |
| GX120Mn13 | SEW | Germany | Steel castings - Austenitic manganese steel castings |
| X120Mn12, 1.3401, A128, X110Mn14 | EN | European | X120Mn12, 1.3401, A128, X110Mn14 High-manganese steels with austenitic structure, characterized by high carbon content - on average 1.00-1.20%, and high Manganese content - approx. |