Steels and nickel alloys for fasteners with specified elevated and/or low temperature properties, used in the chemical, petrochemical, pharmaceutical, machine industries (hydraulic systems) and food industry for valves, flanges, pump parts, springs, heat exchangers, screws and even chains.Austenitic non-magnetic stainless steel with high strength properties - a significant resistance to impact, abrasion and high hardness.The grade can be used for working at elevated temperatures
EN X3CrNiCu18-9-4, 1.4567, 1.4560, X3CrNiCu19-9-2 Enquiry | Print this page
EN X3CrNiCu18-9-4, 1.4567, 1.4560, X3CrNiCu19-9-2 Details
EN X3CrNiCu18-9-4, 1.4567, 1.4560, X3CrNiCu19-9-2 Standard Download
| Category | Type | Grade | Microstructure | Designations |
|---|---|---|---|---|
| Grades | Stainless Steels | X3CrNiCu18-9-4, 1.4567, 1.4560, X3CrNiCu19-9-2 | Austenite | European - EN , EN 10088-1 | EN 10088-3 | EN 10088-5 | EN 10263-5 | EN 10269 | |
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | - | 0.04 | ||
| Si | - | 1.00 | ||
| Mn | - | 2.00 | ||
| P | - | 0.045 | ||
| S | - | 0.015 | ||
| Cr | 17.00 | 19.00 | ||
| Ni | 8.50 | 10.50 | ||
| Mo | - | - | ||
| N | - | 0.11 | ||
| Cu | 3.00 | 4.00 |
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 264 (≥) | 262 (≥) | 44 | 11 | 21 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 331 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 974 (≥) | 114 (≥) | 44 | 32 | 11 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 131 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 897 | 245 | 738 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
| Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |
| Grade | Standard | Country | Application |
|---|---|---|---|
| X3CrNiCu18-9-4 | B.S. | UK | Steels and nickel alloys for fasteners with specified elevated and/or low temperature properties |
| 1.4567 | B.S. | UK | Steels and nickel alloys for fasteners with specified elevated and/or low temperature properties |
| X3CrNiCu18-9-4 | ISO | International | Stainless steels - Chemical composition |
| X3CrNiCu18-9-4, 1.4567, 1.4560, X3CrNiCu19-9-2 | EN | European | Steels and nickel alloys for fasteners with specified elevated and/or low temperature properties, used in the chemical, petrochemical, pharmaceutical, machine industries (hydraulic systems) and food industry for valves, flanges, pump parts, springs, heat |
| X3CrNiCu19-9-2 | B.S. | UK | Steel rod, bars and steel wire for cold heading and cold extrusion - Part 5: Technical delivery conditions for stainless steels |
| 1.4560 | B.S. | UK | Steel rod, bars and steel wire for cold heading and cold extrusion - Part 5: Technical delivery conditions for stainless steels |